Light transmittance and polymerization kinetics of amorphous calcium phosphate composites

• DOI: 10.1007/s00784-016-1880-6
• Publication Date: 2016-06-17T05:44:34Z
• Authors: Matej Par; Danijela Marovic; Hrvoje Skenderovic; Ozren Gamulin; Eva Klaric; Zrinka Tarle
• Keywords: Degree of polymerization

This study investigated light transmittance and polymerization kinetics of experimental remineralizing composite materials based on amorphous calcium phosphate (ACP), reinforced with inert fillers.Light-curable composites were composed of Bis-EMA-TEGDMA-HEMA resin and ACP, barium glass, and silica fillers. Additionally, a commercial composite Tetric EvoCeram was used as a reference. Light transmittance was recorded in real-time during curing, and transmittance curves were used to assess polymerization kinetics. To obtain additional information on polymerization kinetics, temperature rise was monitored in real-time during curing and degree of conversion was measured immediately and 24 h post-cure.Light transmittance values of 2-mm thick samples of uncured ACP composites (2.3-2.9 %) were significantly lower than those of the commercial composite (3.8 %). The ACP composites presented a considerable transmittance rise during curing, resulting in post-cure transmittance values similar to or higher than those of the commercial composite (5.5-7.9 vs. 5.4 %). The initial part of light transmittance curves of experimental composites showed a linear rise that lasted for 7-20 s. Linear fitting was performed to obtain a function whose slope was assessed as a measure of polymerization rate. Comparison of transmittance and temperature curves showed that the linear transmittance rise lasted throughout the most part of the pre-vitrification period.The linear rise of light transmittance during curing has not been reported in previous studies and may indicate a unique kinetic behavior, characterized by a long period of nearly constant polymerization rate.The observed kinetic behavior may result in slower development of polymerization shrinkage stress but also inferior mechanical properties.