Preparation and characterization of Sn-doped β-Ga2O3 homoepitaxial films by MOCVD

• DOI: 10.1007/s10853-015-8893-4
• Publication Date: 2015-02-10T11:48:34Z
• Authors: Xuejian Du; Zhao Li; Caina Luan; Weiguang Wang; Mingxian Wang; Xianjin Feng; Hongdi Xiao; Jin Ma
• Keywords: Monoclinic crystal system

Sn-doped gallium oxide (Ga2O3:Sn) films were deposited on β-Ga2O3 (100) substrates by metal organic chemical vapor deposition method. The Sn concentration was varied from 1 to 12 % (atomic ratio). The influences of Sn-doping concentration on structure, raman, and photoelectric properties of the films were investigated in detail. The obtained films were monoclinic β-Ga2O3 homoepitaxial films. A decrease of about eight orders of magnitude in the film resistivity could be achieved through Sn doping. The 10 % Sn-doped film exhibited the best electrical properties and the lowest resistivity of about 1.20 × 10−1 Ω cm, with the hall mobility value of 12.03 cm2 V−1 s−1obtained. The average transmittances of the β-Ga2O3: Sn films in the visible and UV wavelength ranges were all over 85 %. The optical band gap of the films with different Sn-doping concentrations could be modulated from 4.16 to 4.69 eV.