Effect of pretreatment on microstructure and photocatalytic activity of kaolinite/TiO2 composite

• DOI: 10.1007/s10971-018-4760-5
• Publication Date: 2018-07-30T07:09:42Z
• Authors: Hongliang Xu; Shiping Sun; Sanying Jiang; Hailong Wang; Rui Zhang; Qinfu Liu
• Keywords: 02 engineering and technology; 0210 nano-technology; 7. Clean energy

Kaolinite/TiO2 composites were prepared by using sol-gel method and raw kaolin, pretreated kaolinite and tetrabutyl titanate as the main raw materials. X-ray diffractometer, field-emission scanning electron microscope and infrared spectrometer analysis were carried out to characterize the phase composition and microstructure of the samples. The photocatalytic performance of the kaolinite/TiO2 composites were evaluated by degrading the methylene blue (MB) and phenol aqueous solution, respectively. The results show that intercalation and exfoliation reduced the size and thickness of kaolinite particles. Acid treatment improved the distribution and the loading quantity of TiO2 grains. When the kaolinite/TiO2 composites were calcined at 500 °C, the tetragonal structure of anatase particles of 30–100 nm in size were obtained, but the exfoliated kaolinite crystals were damaged. The degradation rate of MB increased gradually with the extension of photocatalytic reaction time and the enhancement of photocatalyst dosage. The adsorption performance of acid-treated kaolinite/TiO2 composite (AKT) was nearly the same as that of raw kaolin/TiO2 composite (RKT), but that of the exfoliated kaolinite/TiO2 composite (EKT) was the most excellent. The photocatalytic performance of AKT and EKT were better than that of RKT, and AKT exhibited the optimum property. Under a certain photocatalyst dosage and photocatalysis time, the absorption rate and the degradation rate decreased gradually with the enhancement of initial concentration of MB. Similar result was also acquired for the degradation of phenol. Both the acid treating and the exfoliating to kaolinite enhanced the photocatalytic performance of the kaolinite/TiO2 composite photocatalysts, but acid treatment may be more helpful to the preparation of high performance kaolinite/TiO2 composite photocatalyst.