Irradiation-Induced Solute Clustering in a Low Nickel FeMnNi Ferritic Alloy

• DOI: 10.1007/s11340-011-9476-1
• Publication Date: 2011-03-16T22:41:50Z
• Authors: E. Meslin; B. Radiguet; P. Pareige; C. Toffolon; A. Barbu
• Keywords: Embrittlement; Atom probe; Degradation

Understanding the radiation embrittlement of reactor pressure vessel (RPV) steels is required to be able to operate safely a nuclear power plant or to extend its lifetime. The mechanical properties degradation is partly due to the clustering of solute under irradiation. To gain knowledge about the clustering process, a Fe−1.1 Mn−0.7 Ni (at.%) alloy was irradiated in a test reactor at two fluxes of 0.15 and 9 ×1017 nE > 1MeV.m − 2.s − 1 and at increasing doses from 0.18 to 1.3 ×1024 nE > 1MeV.m − 2 at 300°C. Atom probe tomography (APT) experiments revealed that the irradiation promotes the formation in the α iron matrix of Mn/Mn and/or Ni/Ni pair correlations at low dose and Mn–Ni enriched clusters at high dose. These clusters dissolve partially after a thermal treatment at 400°C. Based on a comparison with thermodynamic calculations, we show that the solute clustering under irradiation can just result from an induced mechanism.