Comparison of the Mechanical and Electrochemical Properties of WC-25Co Coatings Obtained by High Velocity Oxy-Fuel and Cold Gas Spraying

• DOI: 10.1007/s11666-014-0123-0
• Publication Date: 2014-07-02T01:45:30Z
• Authors: M. Couto; S. Dosta; J. Fernández; J. M. Guilemany
• Keywords: Cermet

Cold gas spray (CGS) coatings were previously produced by spraying WC-25Co cermet powders onto Al7075-T6 and low-carbon steel substrates. Unlike conventional flame spray techniques (e.g., high-velocity oxy-fuel; HVOF), no melting of the powder occurs; the particles are deformed and bond together after being sprayed by a supersonic jet of compressed gas, thereby building up several layers and forming a coating. WC-Co cermets are used in wear-resistant parts, because of their combination of mechanical, physical, and chemical properties. XRD tests were previously run on the initial powder and the coatings to determine possible phase changes during spraying. The bonding strength of the coatings was measured by adhesion tests. Here, WC-25Co coatings were also deposited on the same substrates by HVOF spraying. The wear resistance and fracture toughness of the coatings obtained previously by CGS and the HVOF coatings obtained here were studied. Their corrosion resistance was determined by electrochemical measurements. It was possible to achieve thick, dense, and hard CGS coatings on Al7075-T6 and low-carbon steel substrates, with better or the same mechanical and electrochemical properties as those of the HVOF coatings; making the former a highly competitive method for producing WC-25Co coatings.