Corrosion and cell viability studies of graphite-like hydrogenated amorphous carbon films deposited on bare and nitrided titanium alloy

• DOI: 10.1016/j.corsci.2014.01.025
• Publication Date: 2014-02-02T14:16:03Z
• Authors: Adélia Moreira Ma...; Ronaldo Junio Cam...; Leo Anderson Meir...; Mariana Ilha; Moema Queiroz Vieira; Douglas Rodrigues...; Fátima Costa Rodr...; Iduvirges Lourdes...; Taíse Matte Manha...
• Keywords: Carbon fibers; Amorphous carbon

This work presents a study of corrosion resistance and cell viability of carbon films on bare and nitrided Ti–6Al–4V. Films deposited on bare alloy significantly improve the corrosion resistance. Unexpectedly, films deposited on nitrided alloy present delamination and cracking after 16 days. We associate film failure with the presence of pores combined with a weak film/substrate interaction that allows diffusion of ions at the interface. We found that films tend to diminish the osteoblastic cell viability and the observed variations on film roughness do not improve cell viability.