Quasi-in-situ STEM-EDS insight into the role of Ag in the corrosion behaviour of Mg-Gd-Zr alloys

• DOI: 10.1016/j.corsci.2018.02.058
• Publication Date: 2018-02-27T13:28:24Z
• Authors: Yu Zhang; Poorwa Gore; Wei Rong; Yujuan Wu; Yuanming Yan; Ruifeng Zhang; Liming Peng; Jian-Feng Nie; Nick Birbilis

Abstract The present paper reports a quasi-in-situ STEM-EDS approach for studying the role of Ag in the corrosion behaviour of Mg-Gd-Zr alloys. Following corrosion, the segregation of O at the interface of the α-Mg matrix and the β phase was observed. Furthermore, Ag-rich particles and the re-deposition of Ag were also observed on the nanoscale. Based on quasi-in-situ STEM-EDS observations herein, the partitioning of Ag into the β phase leads to enhanced localised corrosion, whilst the subsequent formation of Ag-rich particles during the corrosion process leads to enhanced rate of corrosion propagation, with accompanying oxy-hydroxide formation observed upon the Mg-Gd-Ag-Zr.