High-performance and flexible solid-state supercapacitors based on high toughness and thermoplastic poly(vinyl alcohol)/NaCl/glycerol supramolecular gel polymer electrolyte

• DOI: 10.1016/j.electacta.2019.134874
• Publication Date: 2019-09-17T03:24:42Z
• Authors: Shuijiao Peng; Xingzong Jiang; Xiaotong Xiang; Kai Chen; Guoqi Chen; Xiancai Jiang; Linxi Hou
• Keywords: 01 natural sciences; 7. Clean energy; 0104 chemical sciences; 3. Good health

Abstract In this work, the high-performance and flexible solid-state supercapacitors were fabricated based on poly(vinyl alcohol)(PVA)/NaCl/glycerol hydrogel electrolyte and activated carbon electrodes. A novel assembling method was proposed according to the formation properties of PVA/NaCl/glycerol hydrogel electrolyte. PVA/NaCl/glycerol hydrogel electrolyte could be quickly formed in a short time at room temperature. Thus the PVA/NaCl/glycerol solution was coated onto the activated carbon electrodes and the hydrogel electrolyte was in situ formed on the surface of the activated electrodes. Meanwhile, the PVA/NaCl/glycerol hydrogel electrolyte could retain outstanding flexibility and ionic conductivity at a low temperature, which makes the solid-state supercapacitor have excellent low-temperature tolerance. Thus, the electrochemical measurements of the assembled supercapacitor were performed at room temperature and a low temperature of −23 °C, respectively. The flexible supercapacitor can show an outstanding flexibility and electrochemical performance at −23 °C. Its specific capacitance can remain approximately 81.0% of its initial specific capacitance at room temperature and the capacitance retention could keep 90.5% of the initial capacitance retention at −23 °C. It also could be anticipated that this multifunctional flexible supercapacitor with the PVA/NaCl/glycerol hydrogel electrolyte would have broad applications in modern flexible energy storage device.