Preparation of LCST regulable DES-lignin-g-PNVCL thermo-responsive polymer by ARGET-ATRP

• DOI: 10.1016/j.ijbiomac.2021.11.077
• Publication Date: 2021-11-17T11:27:25Z
• Authors: Ruixia Liu; Tingting Ding; Pingping Deng; Xiaofan Yan; Fuquan Xiong; Jienan Chen; Zhiping Wu
• Keywords: Atom-transfer radical-polymerization

To expand the field of high-value utilization of lignin. The degraded deep eutectic solvent lignin-grafted poly (N-Vinyl caprolactam) (DES-lignin-g-PNVCL) was synthesized by modified DES-lignin and NVCL via the combination of activators regenerated by electron transfer-atom transfer radical polymerization (ARGET-ATRP). Fourier transform infrared spectroscopy (FT-IR), 1H NMR, X-ray electron spectroscopy (XPS), dynamic light scattering (DLS), differential scanning calorimeter (DSC) were used to characterize the structure and performance of DES-lignin-g-PNVCL. The results indicated that the PNVCL and DES-lignin-g-PNVCL were successfully prepared by ARGET-ATRP. The lowest critical solution temperature (LCST) of PNVCL was 35.75 °C. Due to different strength of hydrogen bond, different energies were required, so the LCST of the polymer can be regulated. When the molar ratio of phenolic hydroxyl group in degraded DES-lignin to 2-bromoisobutyryl bromide (BiBB) was increased from 1:1 to 1:7, the grafting rate of DES-lignin-Br was increased from 32.87% to 60.84%, and the LCST of DES-lignin-g-PNVCL was decreased from 47.98 °C to 27.88 °C. The LCST of DES-lignin-g-PNVCL was increased from 30.98 °C to 44.64 °C when the addition amount of DES-lignin-Br was increased from 20 mg to 200 mg. The LCST of DES-lignin-g-PNVCL was increased from 27.20 °C to 39.86 °C when the ratio of DMF/water was increased from 1:4 to 4:1. The LCST of DES-lignin-g-PNVCL was decreased from 52.10 °C to 31.02 °C when the concentration of DES-lignin-g-PNVCL was increased from 0.5 mg/mL to 2.5 mg/mL. The equation represented the relationship between LCST and influencing factors was obtained, the good predictability provided a tactics for preparing desired LCST thermo-responsible polymer.