Improved fatigue behavior of low-carbon steel 20GL by applying ultrasonic impact treatment combined with the electric discharge surface alloying

• DOI: 10.1016/j.msea.2016.02.036
• Publication Date: 2016-02-16T13:33:25Z
• Authors: B.N. Mordyuk; G.I. Prokopenko; P.Yu. Volosevich; L.E. Matokhnyuk; A.V. Byalonovich; T.V. Popova
• Keywords: 0203 mechanical engineering; 13. Climate action; 02 engineering and technology

Abstract The effects of severe plastic deformation induced by ultrasonic impact treatment (UIT) and the electric discharge surface alloying (EDSA) with chromium on the stress-controlled fatigue response of low-carbon steel 20GL are studied. The surface microrelief and integrity were analyzed using light microscopy and scanning electron microscopy (SEM). The structural formations in the sub-surface layers were characterized by means of X-ray diffraction analysis and transmission electron microscopy (TEM). The steel specimens underwent UIT, and complex UIT+EDSA and UIT+EDSA+UIT processes demonstrate the fatigue strength magnitudes increased respectively by ~15, ~5 and ~30% on the base of 10 7 cycles in comparison with that for the pristine specimen. SEM analysis of fracture surfaces reveals the subsurface crack nucleation in the UIT-processed specimens instead of superficial crack initiation observed in the pristine and EDSA-processed ones. TEM studies demonstrate that a dislocation-cell structure forms in ferrite grains and partial dissolution of cementite occurs in pearlite grains both at the surface after UIT and in the layer at a depth of 15–25 µm after the UIT+EDSA+UIT process. The enhanced fatigue strength and prolonged lifetime of the low-carbon steel specimens after UIT and UIT+EDSA+UIT processes are concluded to be associated with the subsurface crack nucleation achieved by the following factors: (i) minimized surface roughness and improved integrity of the modified layer; (ii) compressive residual stresses; and (iii) surface hardening coupled with the alloying by chromium and with the formation of the dislocation-cell structure containing the cell walls impenetrable to moving dislocations at cyclic loading.