Influence of oxygen transfer in Hf-based high-k dielectrics on flatband voltage shift

• DOI: 10.1016/j.tsf.2011.10.086
• Publication Date: 2011-10-31T08:51:10Z
• Authors: Toshihide Nabatame; Masayuki Kimura; Hiroyuki Yamada; Akihiko Ohi; Tomoji Ohishi; Toyohiro Chikyow
• Keywords: High-κ dielectric

Abstract We investigated flatband voltage (Vfb) behavior for several Hf-based high-k dielectrics, including HfO 2 , Mg-, and La-incorporated HfO 2 , HfSiO x , and Mg-, La-, and N-incorporated HfSiO x , during the reduction (forming gas annealing: FGA) and oxidation annealing (ODA) processes. A negative Vfb shift appeared in all high-k dielectrics as the FGA temperature increased. In contrast, a positive Vfb shift was observed after the introduction of additional oxygen into the high-k layer during ODA. The oxygen diffusion coefficient (D) values of all samples were estimated using Fick's law. The results showed that the D value of the HfO 2 dielectric was five times as large as that of the HfSiO x dielectric in ODA at 400 °C. Furthermore, the Mg-, La-, and N- incorporated high-k dielectrics exhibited a larger D value compared with the pure high-k dielectrics. These results strongly suggest that the ionicity of high-k dielectrics, which we attribute to a large positive Vfb shift, enhances oxygen diffusion in the high-k layer.