Synthesis, nanostructure and magnetic properties of FeCo-reduced graphene oxide composite films by one-step electrodeposition

• DOI: 10.1016/j.tsf.2015.11.022
• Publication Date: 2015-11-12T16:47:08Z
• Authors: Derang Cao; Hao Li; Zhenkun Wang; Jinwu Wei; Jianbo Wang; Qingfang Liu
• Keywords: 02 engineering and technology; 0210 nano-technology

Abstract FeCo-reduced graphene oxide (FeCo-RGO) composite film was fabricated on indium tin oxide substrate using one-step electrodeposition method. Raman spectroscopy and field emission scanning electron microscope results show that the reduced graphene oxide is coprecipitated with the FeCo film. The energy-dispersive spectrometer results demonstrate that the atomic ratio of Fe/Co in FeCo-RGO composite film is larger than that of the FeCo film under the same fabrication condition. As a result, the FeCo-RGO composite film exhibits good soft magnetic properties and high-frequency properties as well as the FeCo film. The magnetic anisotropy field and saturation magnetization of FeCo-RGO composite film are increased when compared with FeCo film. Furthermore, the ferromagnetic resonance frequency is improved from 2.15 GHz for the FeCo film to 3.9 GHz for the FeCo-RGO composite film.