Anti-reflective surface structures for spinel ceramics and fused silica windows, lenses and optical fibers

• DOI: 10.1364/ome.4.002504
• Publication Date: 2014-11-07T15:41:28Z
• Authors: Lynda E. Busse; Catalin M. Florea; Jesse A. Frantz; L. Brandon Shaw; Ishwar D. Aggarwal; Menelaos K. Poutous; Rajendra Joshi; Jas S. Sanghera
• Keywords: 02 engineering and technology; 0210 nano-technology

Anti-reflective surfaces structures (ARSS) have been successfully fabricated on fused silica windows, lenses and fibers, and spinel ceramics. The reflection loss for spinel was reduced from 7% per surface to 0.9%. For fused silica with ARSS, the reflection loss was reduced to 0.02% near 1 µm. Pulsed laser damage thresholds at 1.06 µm were measured and thresholds as high as 100 J/cm2 were obtained for fused silica windows of up to 10 cm in diameter with ARSS and 850 J/cm2 for silica fibers with ARSS on the end faces. Spinel samples with ARSS showed damage thresholds more than two times higher than that of spinel with traditional AR coatings.