Properties of soil-cement stabilised with deep mixing method

• DOI: 10.1680/grim.2001.5.2.69
• Publication Date: 2009-11-17T20:27:06Z
• Authors: Y. S. Fang; Y. T. Chung; F. J. Yu; T. J. Chen
• Keywords: Soil cement

Engineering properties of soil-cement obtained from the construction site a liquid natural gas (LNG) station are reported in this paper. To increase bearing capacity and to reduce settlements soft ground under pipeline building loads, columns were fabricated with mechanical deep-mixing method. Fourteen days after construction, 50 mm-diameter cylindrical specimens drilled then tested laboratory. Based on experimental results it is found that recovery ratio varies 71% 90%. Shear modulus increased by about 40–140 times as result deep mixing. Uniaxial compressive strengths quite scattered, however, test greater than design strength 2·0 MPa. Compressibility has reduced 45% 90%, modification. Nous donnons dans cet article les propriétés techniques d'un sol-ciment, relevées sur le chantier de d'une gaz naturel liquéfié (GNL). Pour augmenter la portance et réduire tassements du sol tendre sous pipelines charges des colonnes sol-ciment ont été fabriquées en utilisant une méthode mixage profond. Quatorze jours après spécimens cylindriques mm diamètres extraits testés laboratoire. Sur base ces expériences, il apparaît que taux récupération varie entre Le module cisaillement se trouve multiplié par un facteur environ, à cause Les résistances compression uniaxiale sont assez dispersées mais résultats essais supérieurs résistance nominale La compressibilité réduite 45 90% àcause modification sol.