Recently, electromagnetic wireless power transfer (WPT) has emerged as a promising technology for supplying to multiple terminals. Previous studies have devised packet transmission methods, commonly used in telecommunication, analysis. This study develops simulator that calculates the received by integrating power–packet conversion method, based on previous research. The incorporates several scheduling functions facilitate investigation of efficiency power-feeding methods. analyzes efficacy...

A new technique for designing the material composition a powder-type magnetic wood to achieve specific matching frequency an electromagnetic wave absorber is proposed and validated experimentally. The complex permittivity of powder changed by heating until surface carbonized (referred as half- carbonized) has conductive property. alters at which peak absorption takes place. experimental results this study show that characteristics Mn-Zn ferrite (40 volume%) can be controlled adjusting...

Abstract To understand the fuel characteristics of a waste shiitake mushroom bed derived from hardwood chips, moisture content at time disposal and after 1 month, as well its calorific value, ash content, elemental composition, were investigated. The on wet basis (MC w ) was 78% high 63% even month disposal. It is considered that slow drying process caused by low permeability skin bed, therefore, it preferable to crush before drying. Comparing gross value dry with cultivation wood inside...

The purpose of this paper is to demonstrate the electromagnetic wave absorption characteristics powder-type magnetic wood by changing mixing ratios for Mn-Zn ferrite and Ni-Zn powder. results show that matching frequency can be controlled materials thickness board. We obtained close 20 dB over 2.5 GHz-6.2 GHz range. boards used in these experiments satisfy JIS standards surface terms bending strength deflection. from our studies design indoor absorbers a specified frequency.

Abstract Wood-based boards were exposed to an outdoor environment at angles of 90° and 45° the ground surface in order investigate effect exposure angle on board properties. In a study 5-year exposure, effects varied depending type board. Particleboard (PB) oriented strand (OSB) deteriorated faster when compared with 90°, difference was more apparent longer exposure. Five years lowered retention modulus rupture internal bond phenolic resin–bonded PB 15 4 percent, respectively. contrast,...

Summary The mechanisms which cause an improvement in the dimensional stability of particleboards made from steam pretreated particles were investigated aspects potential thickness recoveries densified wood and breakage adhesive bond network particleboards. Since latter would depend on balance between strengths stresses imposed bond, effects steaming temperature (160 to 220°C) quality, recovery stress compressed in-plane swelling investigated. Steam pretreatment was found: 1) reduce...

プレーナー屑を原料とする建築用バインダレス断熱パネル (密度100 kg/m3) を, 厚さ50~150 mmの範囲で製造した。非定常温度スケジュールにおける壁内一次元熱流を測定し, 断熱性と蓄熱性に及ぼすパネル厚さの影響を調べると同時に, 本断熱パネルの熱的性質を市販のグラスウールおよびフェノールフォームと比較した。得られた結果を要約すると, 1) 実用的な厚さ範囲 (100~150 mm) でほぼ一定の熱伝導率 (0.060 W/mK) を示した。2) 同一熱抵抗を持つグラスウールやフェノールと比較して壁体への流入熱量が抑制され, 保温性の優位性が示唆された。3) 熱拡散率 (0.41 × 10-6 m2/s) はグラスウールの約1/2, フェノールフォームの約3/4となり, 蓄熱効果による保温性が期待できる。

When wood based panels are nailed and/or bonded to lumber frame, effects of mechanical restraint on the panel hygroscopic linear expansion (LE) sometimes differ at in-plane biaxial directions. Even adverse effect that LE in one direction becomes larger than its free is recognized when other strongly restrained. To give a better understanding for this phenomenon, study was designed investigate "Poisson's effect" by comparing and LEs uniaxially restrained specimen medium density fiberboard...

製材工場から排出されたスギ，カラマツ，アカマツの樹皮チップを外樹皮部，内樹皮部，付着木部に分離し，無水高位発熱量（Hho）の差異を調べた。灰分の影響を排除すると，樹皮＞木部という発熱量の大小関係が明瞭化された。また，試料の炭素，酸素，水素の組成比から発熱量を推算し，実測値と比較した。その結果，樹皮発熱量の木部に対する優位性は，“木部に対して炭素含量が多く，酸素含量が少ないことに起因する”と解釈された。さらに，化学成分の観点からは，発熱量の最も低い炭水化物と最も高い樹脂成分の構成比率により，樹皮と木部の発熱量の差異が説明可能であった。一方，樹皮チップの部位による低位発熱量の差異は，Hhoにおける差異より大きく，樹皮発熱量の木部に対する優位性は湿潤時に一層高くなることが分かった。さらに，製材工場における樹皮チップの含水率調査結果を用いて，ボイラー燃料としての低位発熱量の変動範囲を推定した。

本断熱パネルの原料選択の拡大を目的に，スギ樹皮小片パネルを製造し，木部小片が原料の場合（スギ木部フレーク小片パネルおよびスギその他の木部プレーナー屑パネル）との性能比較を行った。密度範囲100～180 kg/m3 および3種類の樹皮小片サイズでパネルを製造したところ，断熱性と耐落下衝撃性を両立させる最適パネル密度は，いずれの小片サイズでも140 となった。このときの熱伝導率は約0.07 W/mKであり，同じパネル密度でのスギ木部フレーク小片パネルの熱伝導率よりも若干小さく，耐落下衝撃性も樹皮小片の方が優れた。一方，スギその他の木部プレーナー屑パネルでは，パネル密度を100 程度に下げても耐落下衝撃性が確保され，約0.06 W/mKの熱伝導率が得られているため，スギ樹皮小片パネルの断熱性は木部プレーナー屑パネルよりも劣ることが分かった。

木材－プラスチック成形複合材（WPC）に対して促進耐候性試験（キセノンランプ法：JIS K7350－2）を実施し，WPC の表面劣化現象における，屋外暴露試験に対する促進耐候性試験の促進性および相関性を検討した。促進性および相関性は，試料表面のチョーキング量を表面劣化の指標とし，評価した。促進耐候性試験後にそのままチョーキング量を測定すると，その最大値は屋外暴露試験の場合よりも大きな値をとった。一方，促進耐候性試験後に蒸留水でWPC を超音波洗浄し，その後チョーキング量を測定すると，屋外暴露試験におけるチョーキング量の最大値に近い値をとることが明らかとなった。超音波洗浄した場合における，キセノンランプ法の屋外暴露試験法に対する促進倍率は，およそ７～９であった。促進耐候性試験片の表面層を各種機器分析によって解析したところ，木材とポリオレフィンの劣化がともに生じていることが明らかとなり，これは屋外暴露試験片表面層の機器分析結果と比較的類似していた。したがって，キセノンランプ法による促進耐候性試験によって，屋外暴露試験におけるWPC 表面の劣化状態をある程度再現できることが明らかとなった。

プレーナー屑を型枠中で密度110kg/m3に圧縮し, これを防湿フィルムで被覆した断熱材(木質小片断熱材)を製造した。この断熱材を木造軸組のモデル壁体に充填し, 耐火試験を行って, 遮熱性と柱の断面欠損を調べた。比較対照は中空壁およびグラスウール充填壁とした。その結果, 木質小片断熱材を充填した壁体では, 遮熱性が中空壁やグラスウール充填壁よりも優れ, 準耐火構造相当の遮熱性が認められた。また, 加熱60分後の柱の断面欠損率は, 木質小片断熱材を充填した場合, グラスウール充填壁の約60%に抑制され, 構造安全性の面でも木質小片断熱材の優位性が示唆された。

構造用木質面材の新たな釘側面抵抗試験の提案を目的に，面材張り構面の釘接合部を想定した一面せん断型の釘側面抵抗（LNR）の試験治具を作製してパーティクルボード（PB：厚さ12mm，15mm）のLNRを求め，その値を二面せん断型の試験方法（ASTM D1037）によるLNRと比較した。その結果，一面せん断型のLNRは二面せん断型の4～6割の値となった。釘打ち縁端距離deを12mmから24mmまで増加させた場合，LNRの増加率は二面せん断型よりも一面せん断型の方が小さかった。試験片の幅中央部と隅角部の2種類の釘打ち位置でLNRを比較した場合，どちらの試験方法およびde＝12，18，24mmのいずれの試験条件でも両者の間に有意差は認められなかった。また，促進劣化処理によるLNR残存率は，一面せん断型の方が二面せん断型より2～10％だけ高かった。