A5007511947- Aluminum Alloy Microstructure Properties
- Material Properties and Applications
- Nuclear materials and radiation effects
- Metallurgy and Material Forming
- Metallurgical Processes and Thermodynamics
- Aluminum Alloys Composites Properties
- Metal Alloys Wear and Properties
- Photoreceptor and optogenetics research
- X-ray Diffraction in Crystallography
- High Temperature Alloys and Creep
- Microstructure and Mechanical Properties of Steels
- Metallurgical and Alloy Processes
- nanoparticles nucleation surface interactions
- Crystal Structures and Properties
- Intermetallics and Advanced Alloy Properties
- Advanced Materials Characterization Techniques
- Lipid Membrane Structure and Behavior
- Material Properties and Failure Mechanisms
- bioluminescence and chemiluminescence research
- Advanced materials and composites
- Engineering Diagnostics and Reliability
- Microwave Dielectric Ceramics Synthesis
- Microstructure and mechanical properties
- Chemical Synthesis and Characterization
- biodegradable polymer synthesis and properties
N. I. Lobachevsky State University of Nizhny Novgorod
2015-2024
Tula State University
2014-2021
All Russian Scientific Research Institute of Aviation Materials
2002-2017
The nonequilibrium δnon-phase was originally investigated in the work[1] when studying ageing processes of 1424 alloy ( Al-Li-Mg-system). As shown work[2] this phase may also be formed during cooling from temperature SSHT. precipitates are present 1420 same system[3]. basic structure investigations were carried out on sheets aged accordance with regime: 125°C, 32 hrs. performed by TEM using JEOL JEM 200CX microscope. diffraction patterns crystallographic axes zones close to <110>,...
The Russian 1370 Al-Mg-Si-Cu alloy (analogue of 6056) is an advanced material for the skin and stringers fuselage. However, these alloys are susceptible to intercrystalline corrosion depending on heat treatment regimes. investigations effect heating temperature during solid solution (530-555)°C quenching rate, ageing regimes interval between structure properties sheets were performed. strengthening β (Mg2Si) -phase Q (Al5Cu2Mg8Si6) relationship dependence established. Using dark field...
The fine-fibrous nonrecrystallized structure determines substantial tensile property anisotropy of hot rolled 1424 alloy sheets. In the present work possibility producing a fully recrystallized in cold sheets was investigated. To improve technological plasticity rolling performed after preliminary annealing studied by means determination critical deformation degree at plane strain compression room temperature. phase composition and annealed investigated using TEM X-ray analysis. uniform...
The hydrolysis of powder polyacrylonitrile and copolymers acrylonitrile in order to produce water-soluble polymers is investigated.