Surface and Grain Boundary Coating for Stabilizing LiNi0.8Mn0.1Co0.1O2 Based Electrodes

• DOI: 10.1002/cssc.202400272
• Publication Date: 2024-06-19T06:04:00Z
• Authors: Zahra Ahaliabadeh; Ville Miikkulainen; Miia Mäntymäki; Seyedabolfazl Mou...; Lide Yao; Hua Jiang; Simo Huotari; Timo Kankaanpää; Tanja Kallio; Mattia Colalongo
• Keywords: Cracking; Atomic layer deposition; cracking; nickel-rich positive electrode; 02 engineering and technology; phase transitions; Chemical sciences; grain boundary; Phase transitions; Nickel-rich positive electrode; atomic layer deposition; Lithium titanate; SDG 7 - Affordable and Clean Energy; lithium titanate coating; 0210 nano-technology; Research Article

AbstractThe widespread use of high‐capacity Ni‐rich layered oxides such as LiNi0.8Mn0.1Co0.1O2 (NMC811), in lithium‐ion batteries is hindered due to practical capacity loss and reduced working voltage during operation. Aging leads to defective NMC811 particles, affecting electrochemical performance. Surface modification offers a promising approach to improve cycle life. Here, we introduce an amorphous lithium titanate (LTO) coating via atomic layer deposition (ALD), not only covering NMC811 surfaces but also penetrating cavities and grain boundaries. As NMC811 electrodes suffer from low structural stability during charge and discharge, We combined electrochemistry, operando X‐ray diffraction (XRD), and dilatometry to understand structural changes and the coating protective effects. XRD reveals significant structural evolution during delithiation for uncoated NMC811. The highly reversible phase change in coated NMC811 highlights enhanced bulk structure stability. The LTO coating retards NMC811 degradation, boosting capacity retention from 86 % to 93 % after 140 cycles. This study underscores the importance of grain boundary engineering for Ni‐rich layered oxide electrode stability and the interplay of chemical and mechanical factors in battery aging.