Extremely Compressible Hydrogel via Incorporation of Modified Graphitic Carbon Nitride
Molecular Structure
Nitriles
Static Electricity
02 engineering and technology
0210 nano-technology
01 natural sciences
Hydrogel, Polyethylene Glycol Dimethacrylate
0104 chemical sciences
DOI:
10.1002/marc.201800712
Publication Date:
2018-11-30T14:06:27Z
AUTHORS (5)
ABSTRACT
Extremely compressible hydrogels are fabricated in one pot via sulfonic-acid-modified graphitic carbon nitride (g-CN-AHPA) as a visible light photoinitiator and reinforcer. The show unusual compressibility upon applied stress up to 12 MPa, presenting temporary physical deformation, remain undamaged after removal despite their high water content (90 wt%). Cyclic proves the fatigue resistance of covalently electrostatically reinforced system that possesses tissue adhesive properties, shock resistance, cut little no toxicity.
SUPPLEMENTAL MATERIAL
Coming soon ....
REFERENCES (42)
CITATIONS (25)
EXTERNAL LINKS
PlumX Metrics
RECOMMENDATIONS
FAIR ASSESSMENT
Coming soon ....
JUPYTER LAB
Coming soon ....