Formation of nanosize Li-ferrites from acetylacetonato complexes and their crystal structure, microstructure and order–disorder phase transition

• DOI: 10.1007/s00339-005-3378-y
• Publication Date: 2005-09-28T10:21:59Z
• Authors: M. Vucinic-Vasic; B. Antic; J. Blanusa; S. Rakic; A. Kremenović; A.S. Nikolic; A. Kapor
• Keywords: 02 engineering and technology; 0210 nano-technology; 01 natural sciences; 0104 chemical sciences

Nanosize Li-ferrites were synthesised by the thermal decomposition of an appropriate mixture of complex compounds with acetylacetone - (2,4 pentadione) ligands ([M(AA)x]; M=Li and Fe) at 500 °C. The obtained sample is composed of three phases determined by the standard Rietveld procedure: Li0.5Fe2.5O4 (S.G. P4332), Li1.16Fe3O4 (S.G. Fd 3 m) and LiFeO2 (S.G. Fm 3 m). Cation distribution in nanosize ordered spinel Li0.5Fe2.5O4 deviates from that of the bulk counterpart. Microstructure parameters (crystallite size of ∼23 nm and strain of 3.2526(9)×103) were determined by the Rietveld refinement of the TCH-pV parameters. SEM microphotographs show a particle size of ∼50–60 nm. An order–disorder phase transition in ordered spinel Li0.5Fe2.5O4was studied by DSC measurements and in situ XRPD technique.The temperature of phase transition was found to be 762 °C (DSC) and (±) 7455°C.(XRPD)