Thermally Sprayed Aluminum (TSA) Coatings for Extended Design Life of 22%Cr Duplex Stainless Steel in Marine Environments

• DOI: 10.1007/s11666-012-9879-2
• Publication Date: 2013-01-09T17:47:58Z
• Authors: S. Paul; S. Shrestha; C. M. Lee; M. D. F. Harvey
• Keywords: Pitting Corrosion; Artificial seawater; Duplex (building)

In this article, evaluation of sealed and unsealed thermally sprayed aluminum (TSA) for the protection of 22%Cr duplex stainless steel (DSS) from corrosion in aerated, elevated temperature synthetic seawater is presented. The assessments involved general and pitting corrosion tests, external chloride stress corrosion cracking (SCC), and hydrogen-induced stress cracking (HISC). These tests indicated that DSS samples, which would otherwise fail on their own in a few days, did not show pitting or fail under chloride SCC and HISC conditions when coated with TSA (with or without a sealant). TSA-coated specimens failed only at very high stresses (>120% proof stress). In general, TSA offered protection to the underlying or exposed steel by cathodically polarizing it and forming a calcareous deposit in synthetic seawater. The morphology of the calcareous deposit was found to be temperature dependent and in general was of duplex nature. The free corrosion rate of TSA in synthetic seawater was measured to be ~5-8 μm/year at ~18 °C and ~6-7 μm/year at 80 °C.