Preparation and properties of poly HTBN-based urethane-urea/organo reactive montmorillonite nanocomposites

• DOI: 10.1007/s11706-012-0185-1
• Publication Date: 2012-11-15T23:51:01Z
• Authors: Zai-Feng Li; Yuan Wu; Fu-Tao Zhang; Yu-Yang Cao; Shou-Peng Wu; Ting Wang
• Keywords: 02 engineering and technology; 0210 nano-technology; 01 natural sciences; 0104 chemical sciences

With ultrasonic assistant mixing way, an intercalated mixture of polyol/organo reactive montmorillonite (ORMMT) was pretreated. The prepolymer composed MMT clay was prepared by reaction of polyol/ORMMT mixture with toluene diisocyanate (TDI). The resultant prepolymer reacted with extender (DMTDA) and then the polyurethane-urea/organo reactive montmorillonite (PUU/ORMMT) nanocomposites were obtained. The structure, morphology and properties of PUU/ORMMT nanocomposites were characterized by FT-IR, TEM, AFM, strain-stress machine, TGA, and dynamic mechanical analysis (DMA). The results showed that when the OMMT content is 3%, the PUU/ORMMT nanocomposities performed super mechanical properties. Because of the presence of ORMMT, both T g of the soft segment and tanδ of the PUU increased, and the decomposition temperature for the first step and the second step increased respectively. TEM images showed that the organophilic MMT particles in the PUU composite exhibit a high degree of intercalation and exfoliation.