Fabrication of Fe nanocomplex pillared few-layered Ti3C2Tx MXene with enhanced rate performance for lithium-ion batteries

• DOI: 10.1007/s12274-020-3221-y
• Publication Date: 2020-12-01T18:25:18Z
• Authors: Pengfei Huang; Shunlong Zhang; Hangjun Ying; Wentao Yang; Jianli Wang; Rongnan Guo; Weiqiang Han
• Keywords: 02 engineering and technology; 0210 nano-technology; 7. Clean energy

Pillaring technologies have been considered as an effective way to improve lithium storage performance of Ti3C2Tx MXene. Nevertheless, the pillared hybrids suffer from sluggish Li+ diffusion kinetics and electronic transportation due to the compact multi-layered MXene structure, thus exhibiting inferior rate performance. Herein, the few-layered Ti3C2 MXene (f-Ti3C2 MXene) which is free from restacking can be prepared quickly based on the NH4+ ions method. Besides, Fe nanocomplex pillared few-layered Ti3C2Tx (FPTC) heterostructures are fabricated via the intercalation of Fe ions into the interlayer of f-Ti3C2 MXene. The f-Ti3C2 MXene which is immune to restacking can provide a highly conductive substrate for the rapid transport of Li+ ions and electrons and possess adequate electrolyte accessible area. Moreover, f-Ti3C2 MXene can efficiently relieve the aggregation, prevent the pulverization and buffer the large volume change of Fe nanocomplex during lithiation/delithiation process, leading to enhanced charge transfer kinetics and excellent structural stability of FPTC composites. Consequently, the FPTC hybrids exhibit a high capacity of 535 mAh·g−1 after 150 cycles at 0.5 A·g−1 and an enhanced rate performance with 310 mAh·g−1 after 850 cycles at 5 A·g−1. This strategy is facile, universal and can be extended to fabricate various few-layered MXene-derived hybrids with superior rate capability.