Disproportionation enabling reversible MnO2/Mn2+ transformation in a mild aqueous Zn-MnO2 hybrid battery

• DOI: 10.1016/j.cej.2021.133064
• Publication Date: 2021-10-20T06:27:29Z
• Authors: Huizhen Lv; Yu Song; Zengming Qin; Mingyue Zhang; Duo Yang; Qing Pan; Zhihui Wang; Xinjian Mu; Jianming Meng; Xiaoqi Sun; Xiao-Xia Liu
• Keywords: 02 engineering and technology; 0210 nano-technology; 7. Clean energy

Abstract The disproportionation of the Jahn-Teller (J-T) active manganese oxides (Mn3+) often leads to uncontrollable Mn2+ dissolution, which has been identified as one of the major causes of the performance degradation in conventional Zn-MnO2 batteries. Herein, we use the “unwanted” disproportionation of the Mn3+ cations to realize effective MnO2/Mn2+ transformation, achieving high specific capacity (550 mAh g−1) and good cycling stability (5000 cycles without capacity decay) in a Zn-MnO2 hybrid battery with mild aqueous electrolytes. Mechanism study shows that MnO2 is deposited on the cathode during charging, H+/Zn2+ insertion and disproportionation occur sequentially during discharging, leading to Mn2+ dissolution. The generated high-valence manganese oxides via disproportionation further experience reduction-disproportionation-dissolution, which proceeds repeatedly in the expanded discharge potential to 0 V vs. Zn2+/Zn, resulting in the complete dissolution of the cathodic materials. Our results provide the fundamental understanding on the controversial mechanisms of Zn-MnO2 batteries with mild aqueous electrolytes and highlight the effect of disproportionation in pushing the electrochemical performance of the promising Zn-MnO2 hybrid batteries.