Enhanced piezoelectric performance of BiCl3/PVDF nanofibers-based nanogenerators

• DOI: 10.1016/j.compscitech.2020.108100
• Publication Date: 2020-02-26T16:38:57Z
• Authors: Chong Chen; Zikui Bai; Yunzheng Cao; Mingchao Dong; Kankan Jiang; Yingshan Zhou; Yongzhen Tao; Shaojin Gu; Jie Xu; Xianze Yin; Weilin Xu
• Keywords: 01 natural sciences; 7. Clean energy; 0104 chemical sciences

Abstract BiCl3, because of its promoting the formation of β crystal of PVDF and enhancing the conductivity, has drawn increasing attention in the fields of PVDF piezoelectric applications. The high β-phase concentration was achieved from the nanofiber film of PVDF doped with BiCl3, which enhance the piezoelectric power output of the fiber films. Under vertical vibration, the output piezoelectric voltage of BiCl3/PVDF nanofiber film-based piezoelectric nanogenerator with an optimized ratio of 2 wt% is up to 1.1 V, which is 4.76 times higher than that of pure PVDF fiber piezoelectric nanogenerator. The maximum peak current and power surface density are 2 μA and 0.2 μW cm−2, respectively. The alternating output signals generated from the BiCl3/PVDF fiber film can be used to charge a capacitor through a bridge rectifier and then light up a red LED. The test method had great influence on the piezoelectric outputs of the piezoelectric device. When a piezoelectric device is impacted by a falling ball, it can produce a voltage output of 38 V. This study shows that the BiCl3/PVDF nanofiber film based piezoelectric nanogenerator is a promising mechanical energy harvesters for portable electronic and wearable devices.