Application of the modified electrochemical potentiodynamic reactivation method to detect susceptibility to intergranular corrosion of a newly developed lean duplex stainless steel LDX2101

• DOI: 10.1016/j.corsci.2009.11.020
• Publication Date: 2009-11-14T09:34:44Z
• Authors: Bo Deng; Yiming Jiang; Juliang Xu; Tao Sun; Juan Gao; Lihua Zhang; Wei Zhang; Jin Li
• Keywords: 02 engineering and technology; 0210 nano-technology

Abstract The present work aimed at defining optimal conditions using double loop electrochemical potentiokinetic reactivation (DL-EPR) method for evaluating intergranular corrosion (IGC) susceptibility of lean duplex stainless steel (LDX2101) aged at 700 °C between 3 min and 300 h. The results demonstrated that the modified DL-EPR measurement (solution of 33% H 2 SO 4 + 0.1% HCl at 20 °C and scan rate of 2.5 mV/s) could successfully characterize the interactions between precipitation, chromium depletion and IGC of LDX2101 with high sensitivity and reproducibility. In addition, there was no indication of healing because the effect of formation of chromium-enriched precipitates was more dominative than that of redistribution of chromium in depleted zones.