On the oxidation behavior of (Zr,Nb)2Fe under simulated nuclear reactor conditions

• DOI: 10.1016/j.corsci.2016.08.006
• Publication Date: 2016-08-09T17:54:58Z
• Authors: Junhua Hu; Lei Yang; Guoqin Cao; Yifan Yun; Gaihuan Yuan; Qiang Yue; Guosheng Shao
• Keywords: 02 engineering and technology; 0210 nano-technology; 7. Clean energy

Abstract The corrosion behavior of Zr alloys was affected by second phases, especially by those containing Fe and Nb. Ti 2 Ni-type (Zr,Nb) 2 Fe compound was melted and exposed to H 2 O 2 water solution at 320 °C and 16.4 MPa for 60 h. The oxide layer was analyzed by X-ray diffraction and high-resolution transmission electron microscope (HRTEM). The formation of nano-crystalline tetragonal ZrO 2 (Fe-rich area) and amorphous ZrO 2 (Fe-deficient area) was observed. HRTEM analysis identified α-Fe could stabilize tetragonal ZrO 2 due to the epitaxial growth. ZrxFeyNb alloys with different iron were melted and corroded similarly. The result was consistent with the proposed mechanism.