Evaluation of the high temperature oxidation of W-Cr-Zr self-passivating alloys

• DOI: 10.1016/j.corsci.2018.11.022
• Publication Date: 2018-11-26T17:13:13Z
• Authors: X.Y. Tan; F. Klein; A. Litnovsky; T. Wegener; J. Schmitz; Ch. Linsmeier; J.W. Coenen; U. Breuer; M. Rasinski; P. Li; L.M. Luo; Y.C. Wu
• Keywords: info:eu-repo/classification/ddc/670; 02 engineering and technology; 0210 nano-technology

Abstract W-Cr-Zr systems with different compositions were oxidized in a mixed gas (Ar + 20 vol.% O2) atmosphere at 1000 °C. The power law which was used to describe the oxidation behaviour, indicates that W-11.2wt.%Cr-1.7wt.%Zr has an excellent oxidation behaviour. As analysed from the ten-hour exposure, W-Cr-Zr thin film oxidation shows a self-passivating stage followed by a linear oxidation stage. Furthermore, a study on the addition of zirconium indicates that zirconia particles act as diffusion barriers for the chromium cation diffusion and another function as the nucleation sites for the formation of the initial oxide scale.