High-temperature corrosion performance of HVAF-sprayed NiCr, NiAl, and NiCrAlY coatings with alkali sulfate/chloride exposed to ambient air

• DOI: 10.1016/j.corsci.2019.06.021
• Publication Date: 2019-06-25T09:53:17Z
• Authors: Reza Jafari; Esmaeil Sadeghi
• Keywords: Sulfidation; High-Temperature Corrosion; Nichrome; Chromia

Abstract The high-temperature corrosion of high velocity air-fuel (HVAF) thermal spray Ni21Cr, Ni5Al, and Ni21Cr7AlY coatings was investigated at 600 °C for 168 h in ambient air under KCl and 50-50 mol% KCl–K2SO4 salts. Chlorination-oxidation cycle and breakdown of the corrosion products layer were the dominant corrosion mechanism in the chromia-forming Ni21Cr and Ni21Cr7AlY coatings exposed to KCl. KCl–K2SO4 was less corrosive to the chromia-forming coatings as K2SO4 was less reactive to the protective Cr-rich oxide. The alumina-forming NiAl exhibited a better corrosion performance under KCl, though it partially suffered from selective sulfidation when exposed to the mixed salt.