Investigation of Zr(IV) in LiF–CaF2: Stability with oxide ions and electroreduction pathway on inert and reactive electrodes

• DOI: 10.1016/j.electacta.2013.02.022
• Publication Date: 2013-02-13T04:16:00Z
• Authors: M. Gibilaro; L. Massot; P. Chamelot; L. Cassayre; P. Taxil
• Keywords: Electrochemistry; 0211 other engineering and technologies; 0202 electrical engineering, electronic engineering, information engineering; Génie chimique; Zirconium; 02 engineering and technology; Molten fluoride; Zirconium oxifluorides; Zr-Cu intermetallic compounds

In this work, a detailed electrochemical study of the molten LiF-CaF2-ZrF4 system is provided in the 810-920°C temperature range, allowing the determination of the reduction potential, the diffusion coefficient and the reduction mechanism of dissolved Zr(IV) on an inert Ta electrode. Addition of CaO in the molten salt is shown to cause Zr(IV) precipitation into a mixture of solid compounds, most likely ZrO2 and ZrO1.3F1.4. Underpotential deposition of Zr on Cu and Ni electrodes is also evidenced.