Gas permeation field tests of composite Pd and Pd–Au membranes in actual coal derived syngas atmosphere

• DOI: 10.1016/j.ijhydene.2012.06.053
• Publication Date: 2012-07-28T03:02:49Z
• Authors: Federico Guazzone; Jacopo Catalano; Ivan P. Mardilovich; Jay Kniep; Saurabh Pande; Tony Wu; Robert C. Lambrecht; Subhash Datta; Nikolaos K. Kazan...; Yi Hua Ma
• Keywords: Permeance

Abstract Three large scale (with each a permeable area of 200 cm 2 ) highly structured composite Pd and Pd–Au membranes were prepared and tested in an actual stream of coal derived, but desulfurized, syngas at the National Carbon Capture Center (NCCC) in Wilsonville, Al. The objective of the study was to investigate the long term membrane stability and to establish the long term effects of syngas contaminants in the coal derived syngas other than sulfur compounds on H 2 permeance and selectivity. The large scale membranes had thicknesses ranging from 7 to 14 μm, H 2 permeances ranging from 20 to 28 Nm 3 m −2 h −1 bar −0.5 , and an undetectable He leak before the actual syngas test. In the syngas atmosphere, composite Pd and Pd–Au membranes showed an outstanding H 2 permeance stability at 450 °C and 12.6 bar for approximately 200 h albeit a fast initial decline upon syngas introduction. The fast permeance decline observed at the introduction of the actual syngas was attributed to possible surface and/or bulk poisoning. An exceptionally high H 2 purity level of 99.89% was achieved at 450 °C and 12.6 bar during the entire period of the measurement of over 200 h in syngas atmosphere representing a breakthrough result in the field never reported before with actual syngas from a coal gasification unit.