Microstructure and mechanical properties of Al-12Si and Al-3.5Cu-1.5Mg-1Si bimetal fabricated by selective laser melting

• DOI: 10.1016/j.jmst.2019.03.047
• Publication Date: 2019-08-09T15:39:42Z
• Authors: P. Wang; C.S. Lao; Z.W. Chen; Y.K. Liu; H. Wang; H. Wendrock; J. Eckert; S. Scudino
• Keywords: Bimetal; Selective Laser Melting; Texture (cosmology); Zone melting

Abstract An Al-12Si/Al-3.5Cu-1.5Mg-1Si bimetal with a good interface was successfully produced by selective laser melting (SLM). The SLM bimetal exhibits four successive zones along the building direction: an Al-12Si zone, an interfacial zone, a texture-strengthening zone and an Al-Cu-Mg-Si zone. The interfacial zone ( fiber texture. Electron backscatter diffraction analysis shows that the grains grow gradually from the interfacial zone to the Al-Cu-Mg-Si zone along the building direction. Additionally, a strong fiber texture develops at the Al-Cu-Mg-Si side of the interfacial zone and disappears gradually along the building direction. The bimetal exhibits a room temperature yield strength of 267 ± 10 MPa and an ultimate tensile strength of 369 ± 15 MPa with elongation of 2.6% ± 0.1%, revealing the potential of selective laser melting in manufacturing dissimilar materials.