Tuning thermal expansion by a continuing atomic rearrangement mechanism in a multifunctional titanium alloy

• DOI: 10.1016/j.jmst.2020.11.053
• Publication Date: 2020-12-25T15:22:57Z
• Authors: D.L. Gong; H.L. Wang; E.G. Obbard; S.J. Li; R. Yang; Y.L. Hao
• Keywords: Titanium alloy

Abstract As to multifunctional titanium alloys with high strength and low elastic modulus, thermal training is crucial to tune their thermal expansion from positive to negative, resulting in a novel linear expansion which is stable in a wide temperature range. Aided by the high-order Hooke’s law of elastic solids, a reversible atomic rearrangement mechanism was proposed to explain the novel findings which are unexpected from typical shape memory alloys. To confirm this continuous mechanism, a Ti-Nb based alloy, which possesses a nanoscale spongy microstructure consisting of the interpenetrated Nb-rich and Nb-lean domains produced by spinodal decomposition, was used to trace the crystal structure change by in-situ high energy synchrotron X-ray diffraction analyses. By increasing exposure time, the overlapped diffraction peaks can be separated accurately. The calculated results demonstrate that, in the nanoscale Nb-lean domains, the crystal structure parameters vary linearly with changing temperature along the atomic pathway of the bcc-hcp transition. This linear relationship in a wide temperature range is unusual for first-order martensitic shape memory alloys but is common for Invar alloys with high-order spin transitions. Furthermore, the alloy exhibits smooth DSC curves free of transformation-induced heat peaks observed in shape memory alloys, which is consistent with the proposed mechanism that the reversible transition is of high-order.