9%Cr heat resistant steels: Alloy design, microstructure evolution and creep response at 650°C

• DOI: 10.1016/j.msea.2011.03.037
• Publication Date: 2011-03-16T20:18:59Z
• Authors: D. Rojas; J. Garcia; O. Prat; G. Sauthoff; A.R. Kaysser-Pyzalla
• Keywords: 0203 mechanical engineering; 02 engineering and technology

Abstract In this work 9%Cr alloys were designed supported by computational thermodynamic methods. Two sets of alloys were produced: 9%Cr alloys with 0.1%C and 0.05%C and 9%Cr alloys containing ∼0.03% Ti with 0.1%C and 0.05%C (always wt%). Microstructure investigations showed good agreement with the predicted phases of the thermodynamic modeling. The volume fraction of precipitated M 23 C 6 carbides is directly related to the carbon content of the alloys. For Ti-containing alloys the precipitation of nano-sized Ti-rich MX carbonitrides was observed. The microstructure evolution (sub-grain and particle size) during creep at 650 °C/100 MPa was investigated by STEM-HAADF. The sub-grain size evolution and the coarsening of precipitates (MX carbonitrides, M 23 C 6 and Laves phase) were more pronounced for Ti-containing alloys. 9Cr alloys without Ti and with low carbon content presented the highest creep strength of all investigated alloys.