Optical performance and corrosion resistance of TiN/Ni multiphase cermet by laser cladding

• DOI: 10.1016/j.optlastec.2021.107308
• Publication Date: 2021-06-12T21:21:31Z
• Authors: Jianxin Jiang; Xuming Pang; Jianxin Zhou; Bin Li; Fulin Zhou
• Keywords: 0202 electrical engineering, electronic engineering, information engineering; 02 engineering and technology; 7. Clean energy

Abstract Single-layer Ni-TiN cermet coating was prepared on the surface of stainless steel by spray method-laser cladding. The temperature field of the layer was researched. The reasonable parameters of the laser cladding were P = 900w, V = 3 mm/s, D = 3 mm. The results show that the simulated calculated process parameters are appropriate. In particular, an absorptance (α) of 76.4% and a thermal emissivity (e) of 10% at 300 K were calculated when the weight rate of Ni/TiN is 1:1. After heat treatment at 650℃ for 200 h, the absorptance and emissivity of the coating were 78.8% and 5.2% respectively. The absorption rate and emissivity of the multiphase coating were 80.1% and 1.9%. Compared with the single-phase coating, the multiphase coating has better performance, good thermal stability at high temperature, and stable photothermal conversion efficiency.