Photocatalytic properties of porous TiO2/Ag thin films

• DOI: 10.1016/j.tsf.2007.05.033
• Publication Date: 2007-05-25T12:26:40Z
• Authors: Chung-Chieh Chang; Jing-Yi Chen; Tzu-Ling Hsu; Chung-Kwei Lin; Chih-Chieh Chan
• Keywords: 0103 physical sciences; 02 engineering and technology; 0210 nano-technology; 01 natural sciences

Abstract In this study, nanocrystalline TiO 2 /Ag composite thin films were prepared by a sol–gel spin-coating technique. By introducing polystyrene (PS) spheres into the precursor solution, porous TiO 2 /Ag thin films were prepared after calcination at a temperature of 500 °C for 4 h. Three different sizes (50, 200, and 400 nm) of PS spheres were used to prepare porous TiO 2 films. The as-prepared TiO 2 and TiO 2 /Ag thin films were characterized by X-ray diffractometry (XRD) and by scanning electron microscopy to reveal structural and morphological differences. In addition, the photocatalytic properties of these films were investigated by degrading methylene blue under UV irradiation. When PS spheres of different sizes were introduced after calcination, the as-prepared TiO 2 films exhibited different porous structures. XRD results showed that all TiO 2 /Ag films exhibited a major anatase phase. The photodegradation of porous TiO 2 thin films prepared with 200 nm PS spheres and doped with 1 mol% Ag exhibited the best photocatalytic efficiency where ∼ 100% methylene blue was decomposed within 8 h under UV exposure.