Improvement of white organic light emitting diode performances by an annealing process

02 engineering and technology 0210 nano-technology 7. Clean energy
DOI: 10.1016/j.tsf.2009.02.140 Publication Date: 2009-03-10T08:58:34Z
ABSTRACT
Abstract White organic light emitting diode (OLED) devices with the structure ITO/PHF:rubrene/Al, in which PHF (poly(9,9-di-n-hexylfluorenyl-2,7-diyl)) is used as blue light emitting host and rubrene (5,6,11,12-tetraphenylnapthacene) as an orange dye dopant, have been fabricated. Indium tin oxide (ITO) coated-glass and aluminium were used as anode and cathode, respectively. The devices were fabricated with various rubrene-dopant to obtain a white light emission. The OLED device that composed of several concentrations of rubrene-doped PHF film was prepared in this study. It was found that the concentration of rubrene in the PHF-rubrene thin film matrix plays a key role in producing the white color emission. In a typical result, the device composed of 0.06 wt.% rubrene-dopant produced the white light emission with the Commission Internationale de L'Eclairage (CIE) coordinate of (0.30,0.33). The turn-on voltage and the brightness were found to be as low as 14.0 V and as high as 6540 cd/m 2 , respectively. The annealing technique at relatively low temperature (50 °C, 100 °C, and 150 °C) was then used to optimize the performance of the device. In a typical result, the turn-on voltage of the device could be successfully reduced and the brightness could be increased using the annealing technique. At an optimum condition, for example, annealed at 150 °C, the turn-on voltage as low as 8.0 V and the brightness as high as 9040 cd/m 2 were obtained. The mechanism for the improvement of the device performance upon annealing will be discussed.
SUPPLEMENTAL MATERIAL
Coming soon ....
REFERENCES (30)
CITATIONS (19)
EXTERNAL LINKS
PlumX Metrics
RECOMMENDATIONS
FAIR ASSESSMENT
Coming soon ....
JUPYTER LAB
Coming soon ....