Enhancement of carrier mobility in all-inkjet-printed organic thin-film transistors using a blend of poly(3-hexylthiophene) and carbon nanoparticles

• DOI: 10.1016/j.tsf.2011.05.071
• Publication Date: 2011-06-18T22:36:23Z
• Authors: Chih-Ting Lin; Chun-Hao Hsu; Iu-Ren Chen; Chang-Hung Lee; Wen-Jung Wu
• Keywords: Electron Mobility; Inkjet Printing; Organic semiconductor

Abstract To enhance the carrier mobility of all-inkjet-printed organic thin film transistors, we fabricated devices that incorporated poly(3-hexylthiophene) (P3HT) and carbon nanoparticles (CNPs). The fabricated devices had an on/off ratio of 104, which is one order less than that of pristine organic thin-film transistors (OTFTs). The maximum carrier mobility as high as 0.053 cm2/V-s was achieved for a CNP/P3HT weight–weight ratio of 7/100. This degree of mobility is 10 times greater than average mobility of pristine P3HT-OTFTs. X-ray diffraction and scanning electron microscopy images reveal that the carrier mobility was enhanced by reducing the injection barrier and enhancing the carrier injection. This work demonstrates the feasibility of all-inkjet-printed OTFT technology.