Co-Construction of Solid Solution Phase and Void Space in Yolk–Shell Fe0.4Co0.6S@N-Doped Carbon to Enhance Cycling Capacity and Rate Capability for Aluminum-Ion Batteries

• DOI: 10.1021/acsami.1c24510
• Publication Date: 2022-02-03T14:40:57Z
• Authors: Jiening Zheng; Shunlong Ju; Guanglin Xia; Hongge Pan; Xuebin Yu
• Keywords: 01 natural sciences; 0104 chemical sciences

Rechargeable aluminum-ion batteries (AIBs), using low-cost and inherent safety Al metal anodes, are regarded as promising energy storage devices next to lithium-ion batteries. Currently, one of the greatest challenges for AIBs is to explore cathodes suitable for feasible Al3+ insertion/extraction with high structure stability. Herein, a facile co-engineering on solid solution phase and cavity structure is developed via Prussian blue analogues by a simple and facile sulfidation strategy. The obtained uniform yolk-shell Fe0.4Co0.6S@N-doped carbon nanocages (y-s Fe0.4Co0.6S@NC) display a high reversible capacity of 141.3 mA h g-1 at 500 mA g-1 after 100 cycles and a good rate capability of 100.9 mA h g-1 at 1000 mA g-1. The improved performance can be mainly ascribed to the dual merits of the composite; that is, more negative Al3+ formation energy and improved Al3+ diffusion kinetics favored by the solid solution phase and Al3+ insertion/extraction accommodable space stemmed from the yolk-shell structure. Moreover, the reaction mechanism study discloses that the reaction involves the intercalation of Al3+ ions into Fe0.4Co0.6S to generate AllFemConS and elemental Fe and Co.