Highly Stretchable and Highly Conductive PEDOT:PSS/Ionic Liquid Composite Transparent Electrodes for Solution-Processed Stretchable Electronics

• DOI: 10.1021/acsami.6b11988
• Publication Date: 2016-12-19T12:09:03Z
• Authors: Mei Ying Teo; Nara Kim; Seyoung Kee; Bong Seong Kim; Geunjin Kim; Soonil Hong; Suhyun Jung; Kwanghee Lee
• Keywords: 02 engineering and technology; 0210 nano-technology

Stretchable conductive materials have received great attention owing to their potential for realizing next-generation stretchable electronics. However, the simultaneous achievement of excellent mechanical stretchability and high electrical conductivity as well as cost-effective fabrication has been a significant challenge. Here, we report a highly stretchable and highly conducting polymer that was obtained by incorporating an ionic liquid. When 1-ethyl-3-methylimidazolium tetracyanoborate (EMIM TCB) was added to an aqueous conducting polymer solution of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS), it was found that EMIM TCB acts not only as a secondary dopant but also as a plasticizer for PEDOT:PSS, resulting in a high conductivity of >1000 S cm-1 with stable performance at tensile strains up to 50% and even up to 180% in combination with the prestrained substrate technique. Consequently, by exploiting the additional benefits of high transparency and solution-processability of PEDOT:PSS, we were able to fabricate a highly stretchable, semitransparent, and wholly solution-processed alternating current electroluminescent device with unimpaired performance at 50% strain by using PEDOT:PSS/EMIM TCB composite films as both bottom and top electrodes.