Control and Monitoring of Dye Distribution in Mesoporous TiO2 Film for Improving Photovoltaic Performance

• DOI: 10.1021/acsami.6b15488
• Publication Date: 2017-01-06T21:56:12Z
• Authors: Byung-Man Kim; Hyun-Gyu Han; Jeong Soo Kim; HyeonOh Shin; Tae-Hyuk Kwon
• Keywords: 621; 02 engineering and technology; 0210 nano-technology; 7. Clean energy

Dye distribution in a mesoporous TiO2 film is a key factor in the performance of dye-sensitized solar cells, but there has been little research on it. Here we report even dye distribution within the porous TiO2 film achieved by a physical driving force of gas flow. Gas-assisted dye arrangement, gas bubbling soaking (GBS), significantly accelerates the dye infiltration compared to conventional overnight soaking (OS). As a demonstration, we investigated the time-dependent dye infiltration using plasmon sensors. GBS produces an even vertical dispersion throughout the film, as illustrated by time-of-flight secondary ion mass spectrometry depth profiles. For devices using a 7-μm-thick active layer and a ruthenium-based dye (N719), only 15 min of GBS treatment produced better power conversion efficiency (PCE) than the optimal result from OS treatment (15 h), despite a lower dye capacity. Dual-GBS treatment (20 min for N719 and 10 min for YD2, a porphyrin dye) produced the best PCE (9.0%) in the device, which was ∼17% higher than that treated with dual-OS (10 h for N719 and 5 h for YD2). Such improvements are associated with reduced dye-free sites inside the porous TiO2 film after GBS treatment, leading to faster charge transport and slower charge loss.