Phase transformations in the system Cu-Zn-Al under conditions far from equilibrium

• DOI: 10.1063/1.4937826
• Publication Date: 2016-01-16T17:14:21Z
• Authors: Anatolii Klopotov; Yuri Ivanov; Viktor Vlasov; Nikolai Dedov; Oleg Loskutov
• Keywords: цинковые сплавы; порошковые сплавы; фазовые превращения; твердые растворы на основе меди; 02 engineering and technology; многофазные материалы; 0210 nano-technology; алюминиевые сплавы

It is shown that the alloy Cu-Zn-Al is a multiphase material. Under equilibrium conditions this alloy can form an α-phase (FCC crystalline lattice) and a β-phase (simple cubic crystalline lattice) based on copper. The possibility of formation of a γ-phase due to a three-component alloy composition is revealed. It is established that different chemical composition of the copper-based solid solution (alloys with zinc or alloys with aluminum), different concentration of the second element in a solid solution leads to the fact that within the same type of the crystalline lattice there is a certain amount of α- and γ-phases, differing in the parameter value of the crystalline lattice. The possibility of formation of powder alloys with an x-ray amorphous and a nanocrystalline structure using the plasma chemical synthesis methods is demonstrated. A wide variety of binary phases, each with different concentrations of zinc and aluminum in a solid copper-based solution is revealed. These results indicate that plasma-chemical synthesis of metal alloy powders is accompanied by separation of elements. Powders of the ternary composition are not detected.