This paper presents an analysis of the current state processing lead-zinc ores from Koskudyk deposit (Kazakhstan). At present, polymetallic are being extracted Ridder-Sokolnoye, Zyryanovskoye, Maleevskoye, and Achisai deposits. However, reserves rich easily beneficiable depleted, supply raw materials developed deposits does not exceed 25 years. As a result, more complex difficult-to-enrich oxidized mixed involved in production, extraction non-ferrous metals these significant technological...

The progressive depletion of high-grade sulfide ores necessitates the development effective enrichment methods for oxidized lead–zinc ores. This study investigates application sulfidization flotation from Koskuduk deposit, focusing on use calcium polysulfide (CaSₓ) as an alternative to conventional sodium sulfide. Laboratory tests demonstrated that a CaSₓ dosage 700 g/t led superior recovery rates lead (53.56%) and silver (66.1%) compared Mineralogical chemical analyses confirmed dominance...

The experiment was carried out on the copper-molybdenum ore of Shatyrkul-Zhaysan cluster. Shatyrkul field is located in Shuisky district Zhambyl region (Republic Kazakhstan), 35 km east Birlik station and one sites To conduct research firing molybdenum industrial products, a product with yield 0.07%, content 22.23% extraction 74.91% from developed. development rational method for extracting poor raw materials would significantly expand material base, increase into final thereby reducing its...

In the face of global depletion natural resources and increasing demand for sustainable development, processing industrial waste, such as tailings from plants, is becoming essential. This study focuses on combined technologies, including flotation concentration concentrate processing, allowing efficient recovery valuable components. aims to investigate possibility thermochemical enrichment opening low-grade copper plants with transfer silicon rhenium in form silicate-ions perrhenate-ions...

The solution to a specific technological problem is combined with the methodological development of nonlinear multifactorial relationship justify boundaries its extrapolation beyond experimental range used. White soot was produced through two-stage carbonization silicate (composition, g/l: Na2O = 126.5, SiO2 107.7, Al2O3 3.1), obtained after processing waste tailings carbon dioxide in recirculation system. influence deposition duration, temperature, and final pH value pulp on formation...

This research investigates the hydrometallurgical processing of molybdenum middlings extracted from copper-molybdenum ore in Shatyrkul-Zhaysan cluster Kazakhstan. A intermediate obtained after selective flotation concentrate was used, with a recovery 0.07%, content 22.23% and an extraction 74.91%. The mineralogical analysis shows molybdenite chalcopyrite as main minerals. In experiments, atmospheric leaching nitric acid single-stage two-stage countercurrent processes investigated to optimize...

A long period of deposit development leads to a reduction in the volume balance reserves ores, while accumulation waste (tailings) from mining and processing production increases. In connection with this, an urgent problem is tailings, which can serve as additional source commercial products non-ferrous metals. The set objectives be achieved by implementing comprehensive extraction valuable components, reducing fuel, energy costs at stage low-temperature sintering produce white soot (grade...

One of the processes complete and complex extraction valuable components is desiliconization final tailings to increase content concentrate obtain marketable products in form white soot copper cathode. This study aimed investigate possibility further from sulfuric acid solution obtained after thermochemical enrichment rough on a temperature range 300-500°C. Acorga M5774 extractant Elixore 205 diluent served extract pregnant containing 9.59 g/l 24.6 iron. The performance parameters involved...

The article presents the results of thermochemical enrichment waste copper tailings. Studies on sintering concentrate with alkali have established formation silicate and sodium aluminosilicate. extraction silicon into solution, depending temperature in range 250-500°C, increases from 59,96% to 70,40%. After water leaching cake under following conditions: L:S = 3:1 60°C; duration 60 minutes, content average 1,2 times.To isolate white soot a carbon dioxide was used as neutralizing agent. White...

Рассмотрена проблема обогащения лежалых хвостов сложного вещественного состава. Отмечена актуальность регулирования окислительно-востановительного потенциала для вовлечения в валовую переработку сульфидных, смешанных и окисленных частей хвостов. Комплекс проведенных исследований позволил разработать технологические схемы на основе (далее ОВП). Исследования проведены окисленной части с содержанием меди 0,35% со степенью окисленности 65,52%. Лабораторным экспериментом определено, что флотации...

Отвальные медные хвосты хвостохранилищ Жезказганской обогатительной фабрики являются труднообогатимыми. Трудности в обогащении данных хвостов связаны с особенностями их вещественного состава: тонкая зернистость и эмульсионная вкрапленность рудных минералов друг друге, наличие большого количества флотационно-активной пустой породы, высокое содержание тонкодисперсной субмикроскопической меди отвальных хвостах. Для снижения флотационной активности породы было принято решение включить цикл...

На сегодняшний день отсутствует экономически целесообразная технология переработки лежалых медных хвостов. Однако данный техногенный вид сырья кроме меди содержит железо, серебро и диоксид кремния, в связи с этим проведены лабораторные исследования по определению оптимального флотационного режима, позволяющего эффективно извлекать медь черновой концентрат из хвостов обогатительной фабрики. Предложенная схема включает предварительную классификацию последующей медной флотацией. Данный вариант...

Проблемы, с которым приходится сталкиваться горнодобывающей промышленности для достижения утилизации отвальных хвостов в соответствии принципами экономики замкнутого цикла, включает себя улучшение довольно ограниченных знаний о минералогии, концентрации примесей и объём хвостохранилищах. Также необходимо разработка технологий, чтобы сделать процесс экономически целесообразным. Для улучшения показателей операции измельчения оказать существенное влияние на обогащение ценных компонентов было...

В связи с истощением природных ресурсов, загрязнением окружающей среды отходами и площадью складирование хвостов в отвалы актуальной задачей на сегодняшний день является переработка техногенного минерального сырья. Техногенное минеральное сырьё обладает высокой экономической ценностью одним из важнейших резервов увеличения ресурсов без значительных капиталовложений разработку месторождений. Исходная проба лежалых предоставлена первичными рудными минералами продуктами металлургического...